https://repositorio.utn.edu.ec/handle/123456789/19542| Título : | Investigación de material cerámico a base de tio2 obtenido a temperatura ambiente |
| Title : | Room-temperature synthesis of titanium dioxide (TiO₂)-based ceramic materials |
| Autor : | Vera Serna, Pedro López Castro, Tania Luna González, Ricardo |
| Orcid: | https://orcid.org/0000-0001-7085-7374 https://orcid.org/0000-0003-4514-4756 |
| Tipo docuemento: | Article |
| Palabras clave : | TRABAJO;INVESTIGACIÓN;ENERGÍA;ANÁLISIS |
| Keywords : | WORK;RESEARCH;ENERGY;ANALYSIS |
| Fecha de publicación : | 8-abr-2026 |
| Fecha de creación : | 2-ene-2023 |
| Editorial : | Proyecta Revista Científica |
| Resumen : | En este trabajo se presentan los resultados de la investigación del producto obtenido después de 7 horas de molienda de Fe2O3 y TiO2 en un molino de alta energía, ello permitió hacer la discusión de los cambios estructurales y morfológicos, utilizando Difracción de Rayos, Microscopia Electrónica de Barrido y análisis de la Distribución de Tamaño de Partícula con un analizador para este fin, para ello se utilizó un baño ultrasónico y se realizó todo a temperatura ambiente, lo cual suma a las actividades de química verde en la cual no se utilizaron ácidos u otros compuestos de alto riesgo, el producto se puede utilizar después de su obtención, evitando los altos consumos de energía de manera tradicional que normalmente utilizan temperaturas muy altas, se obtuvieron tamaños nanométricos, formas irregulares y los cambios observados en Difracción de Rayos X permiten observar que el material ha modificado sus propiedades con el proceso de química verde. |
| Abstract: | In this work, the results of the investigation of the product obtained after 7 hours of milling Fe2O3 and TiO2 in a high-energy ball milling process are presented, this allowed the discussion of the structural and morphological changes,using X-Ray Diffraction, Scanning Electron Microscopy and the Analysis of the Particle Size Distribution with an analyzer for this purpose, for which an ultrasonic bath was used and everything was done at room temperature, which adds to the green chemistry activities in which they were used any acids or other high-risk compounds, the product can be used after obtaining it, avoiding high energyconsumption in the traditional way that normally uses very high temperatures. Nanometric sizes and irregular shapes were obtained and the changes observed inX-Ray Diffraction allow us to observe that the material has modified its properties with the green chemistry process. |
| URI : | https://repositorio.utn.edu.ec/handle/123456789/19542 |
| Url del recurso: | https://grepxa.mx/wp-content/uploads/2023/03/vol-11.pdf |
| ISSN : | 2683-331X |
| Ciudad. País: | Ibarra. Ecuador |
| Grado Académico: | N/A |
| Aparece en las colecciones: | Artículos |
Ficheros en este ítem:
No hay ficheros asociados a este ítem.
Este ítem está protegido por copyright original |
Este ítem está sujeto a una licencia Creative Commons Licencia Creative Commons